High
Alumina Bricks |
Alumina-Magnesia-Carbon Brick
|
Made
of 96-98% MgO electric fused magnesite, super quality bauxite
and 194-196 large crystal natural flake graphite, with antioxidation
addictives and special resin bond. With superior resistance
to slag, corrossion, oxidation, thermal shock and constructional
spalling etc.Providing customer oriented and cost effective
designing, manucfacuring, exporting of the alumina magnesia
carbon bricks .This type of new products used as lining
material in the various ladles, LFV refining furnace and
LF ladles have experienced an average lifetime from 70 heats
to 130 heats in the past 3 years.
|
Alumina-spinel-carbon brick
|
Item
Index |
Al2O3%
¡Ý |
MgO%
¡Ý |
C%
¡Ý |
A.P.(%) |
B.D.
(g/cm3) |
C.C.S
(Mpa) |
Refactorines
Under load¡Ý |
| LLJT-60 |
60 |
12 |
8 |
8 |
|
45 |
1650 |
| LLJT-55 |
55 |
5-10 |
5 |
10 |
|
40 |
1600 |
| LLJT-50 |
50 |
5-10 |
5 |
18 |
|
40 |
1550 |
High-Alumina
Product Series For Blast Furnace
|
It
is one of our main products whose main mineral component is
mullite and corundum phases, with excellent high temperature
physical properties and chemical corrosion resistance, widely
used in every part of blast furnace lining with good work
ability. It has been used in large volume blast furnace with
a good result. |
|
Index
Item |
High Alumina brick
For blast furnaces |
High-Alumina
Carbon brick for
blast furnaces |
Refractories for
blast furnaces
¡°ceramic cup¡± |
High Alumina
brick for hot
stoves |
| GL-55 |
GL-65 |
LGL-75 |
Unfired
Al2O3-C |
Fired
Al2O3-C |
Mullite
Bonded
Corundum brick |
Combined corundum
brick |
Mullite
brick |
RL-65 |
RL-55 |
| Al2O3¡Ý |
55 |
65 |
75 |
60 |
60 |
85 |
78 |
70 |
65 |
55 |
| Fe2O3¡Ü |
2.0 |
2.0 |
2.0 |
2 |
2 |
|
|
|
|
|
| Refractoriness ¡Ý |
1770 |
1790 |
1790 |
1790 |
1790 |
|
|
|
1790 |
1700 |
| Refractoriness under load¡Ý |
1480 |
1500 |
1520 |
1650 |
1650 |
1700 |
1660 |
1700 |
1500 |
1470 |
| Liner
change after reheating
1500¡æx2h) |
0-0.2 |
0-0.2 |
0-0.2 |
|
|
¡À0.2 |
¡À0.2 |
¡À0.2 |
+0.1
-0.4 |
+0.1
-0.4 |
| C.C.S
(Mpa) |
49.0 |
58.8 |
70 |
60 |
60 |
90 |
98 |
88 |
49.0 |
44.1 |
|
High Alumina bricks for EAF and Ladles
|
Index
item |
High
alumina brick
for EAF roof |
Unfired high
alumina
brick for EAF roof |
Pre-masonry
high
alumina brick for
central area of EAF |
| LDL-80 |
DL-80 |
DL-75 |
LBDL-80 |
LBDL-75 |
LZDL-80 |
LZDL-75 |
|
Al2O3%¡Ý |
80 |
80 |
75 |
80 |
75 |
80 |
75 |
|
Refractoriness
under load |
1550 |
1550 |
1530 |
1560(T2) |
1530(T2) |
1520 |
1500 |
|
Linear change
after reheating |
0-0.3 |
0-0.3 |
0-0.4 |
|
|
0-0.5 |
0-0.5 |
|
C.C.S
(Mpa) |
78 |
78.5 |
68.6 |
60 |
60 |
50 |
|
|
Index Item |
High alumina brick for ladle
|
Unfired high alumina
brick for ladle |
| LCL-55 |
CL-75 |
LCL-80 |
LCL-85 |
CBL-75 |
CBL-80 |
|
Al2O3%¡Ý |
55 |
75 |
80 |
85 |
75 |
80 |
|
Refractoriness
Under load |
1470 |
1510 |
1530 |
1560 |
1530 |
1560 |
|
Linear change
After reheating |
| |